MIM-Fe2Ni
Fe2Ni alloy has good mechanical properties, corrosion resistance and high temperature stability. It can change its shape under the action of an externally applied magnetic field, but it can return to its original shape after removing the magnetic field. It is an intelligent material with broad application prospects. Widely used in industrial automation, MEMS, medical equipment, intelligent buildings, etc.
Chemical Content
- MIM-Fe2Ni
- MIM 4605
- MIM-Fe82Ni
- MIM-2200(as sintered)
| MIM-Fe2Ni | Density | UTS.Mpa | Y.S.(0.2%),Mpa | Elongation(in 25.4mm)% | Macro (apparent0 | Micro(converted) |
| 7.5 | 280 | 115 | 25 | 55 HRB | ≥50HRC |
| Feed | OSF | |||||
| C | Ni | Mo | Si | Fe | ||
| FDC4605A | 0.4-0.6 | 1.5-2.5 | 0.2-0.5 | ≤1.00 | Bal | 1.216 |
| FDC4605B | 0.4-0.6 | 1.5-2.5 | 0.2-0.5 | ≤1.00 | Bal | 1.2 |
| FDC4605C | 0.4-0.6 | 1.5-2.5 | 0.2-0.5 | ≤1.00 | Bal | 1.19 |
| FDC4605DE | 0.4-0.6 | 1.5-2.5 | 0.2-0.5 | ≤1.00 | Bal | 1.185 |
| FDC2200MA | ≤0.10 | 1.5-2.5 | 0.2-0.5 | ≤1.00 | Bal | 1.216 |
| MIM-Fe82Ni | Density | UTS.Mpa | Y.S.(0.2%),Mpa | Elongation(in 25.4mm)% | Macro (apparent0 | Micro(converted) |
| 7.5 | 450 | / | 12 | 84 HRB | ≥50HRC |
| MIM-2200 | Density | UTS.Mpa | Y.S.(0.2%),Mpa | Elongation(in 25.4mm)% | Macro (apparent0 | Micro(converted) |
| 7.65 | 290 | 125 | 40 | 45HRB | / |