MIM-2200 (as sintered)
MIM-2200 is made by adding appropriate amount of carbon powder to 316L stainless steel powder and going through multiple processes such as high temperature sintering, deformation and annealing. The compacted material of MIM-2200 has high density, which can meet the requirements of advanced applications, and is especially suitable for applications that require precision forming and processing, such as medical, electronics, automobiles, video games, batteries and other industries.
Chemical Content
- MIM-2200 (as sintered)
- MIM-4605
- MIM-Fe2Ni
- MIM-Fe82Ni
| MIM-2200 | Density | UTS.Mpa | Y.S.(0.2%),Mpa | Elongation(in 25.4mm)% | Macro (apparent0 | Micro(converted) |
| 7.65 | 290 | 125 | 40 | 45HRB | / |
| Feed | OSF | |||||
| C | Ni | Mo | Si | Fe | ||
| FDC4605A | 0.4-0.6 | 1.5-2.5 | 0.2-0.5 | ≤1.00 | Bal | 1.216 |
| FDC4605B | 0.4-0.6 | 1.5-2.5 | 0.2-0.5 | ≤1.00 | Bal | 1.2 |
| FDC4605C | 0.4-0.6 | 1.5-2.5 | 0.2-0.5 | ≤1.00 | Bal | 1.19 |
| FDC4605DE | 0.4-0.6 | 1.5-2.5 | 0.2-0.5 | ≤1.00 | Bal | 1.185 |
| FDC2200MA | ≤0.10 | 1.5-2.5 | 0.2-0.5 | ≤1.00 | Bal | 1.216 |
| MIM-Fe2Ni | Density | UTS.Mpa | Y.S.(0.2%),Mpa | Elongation(in 25.4mm)% | Macro (apparent0 | Micro(converted) |
| 7.5 | 280 | 115 | 25 | 55 HRB | ≥50HRC |
| MIM-Fe82Ni | Density | UTS.Mpa | Y.S.(0.2%),Mpa | Elongation(in 25.4mm)% | Macro (apparent0 | Micro(converted) |
| 7.5 | 450 | / | 12 | 84 HRB | ≥50HRC |